Plastics processing
UFG srl carries out plastic processing (better known as termpoplastics) of all kinds and for different needs, using plastic materials that meet the needs of each customer, such as PVC, POMc, Nylon, Polyzene, Plexiglass, polycarbonate, etc..
Thermoplastic Temperature Chart
Thermoplastic polymers are polymers formed by linear or slightly branched chains, not tied together with each other; it is therefore sufficient to increase the temperature to bring them to a viscous state and thus form them.
Each time the heating and forming operation is repeated, the material loses some of its features.
From the nature of the material if amorphous or semi-crystalline and the required working temperature, you can identify the most suitable material to meet the needs required in the following table.
These are some of the plastic materials that fall within our plastic processes that make up the pyramid of thermoplastics:
PBI, PI, TPI, PAI, PES, PPSU, PEI, PSU, PC-HT, PEK, PEEK, LCP, PPS, PFA, PTFE, EFTE, PCTFE, PVDF, PC, PA 46, PET, PA 66, PBT, PA6, POM, PMP, PA 12, PPE, PMMA, PS, ABS, SAN, PE, PP
Amorphous thermoplasts:
SUPER POLYMERS: PBI, PI, TPI, PAI, PES, PPSU, PEI, PSU, PC-HT
TECNOPOLYMERI: PC
STANDARD POLYMERS: PPE MOD., PMMA, PS, ABS, SAN
Semicrystalline thermoplastic:
SUPER POLYMERS: PEK, PEEK, LCP, PPS, PFA, PTFE, EFTE, PCTFE, PVDF
TECNO POLYMERS: PA 46, PET, PA 66, PBT, PA 6, POM, PMP, PA 12
STANDARD POLYMERS: PE, PP
Datasheet
PA 6 G-HS
EP GC 202
Type of material: laminated with fiberglass fabric and epoxy resins
Characteristics: Typical yellow-green colour
Use: used for general mechanical and electrical applications, FR = Flame retardant. Spacers, rings, insulators, contactors.
Assortment: slabs and or drawing parts.
Mechanic | Value | Unit | Test Type |
Density | 1.15 | g/cm3 | DIN EN ISO 1183 |
Yield strength | 90/65 | MPa | DIN EN ISO 527 |
Elongation at break | 30/80 | % | DIN EN ISO 527 |
Traction elastic modulus | 3000/1700 | MPa | DIN EN ISO 527 |
Flexible elastic modulus | 3300/2300 | MPa | DIN EN ISO 178 |
Bending resistance | 120/40 | MPa | DIN EN ISO 178 |
Impact resistance | N.R. | kJ/m2 | DIN EN ISO 179 |
Slotted impact resistance | >4 | kJ/m2 | DIN EN ISO 179 |
Hardness with ball penetration H358/30 | 170 | MPa | ISO 2039-1 |
Creep traction test: 1% elongation | >7 | MPa | DIN 53 444 |
Dynamic dry friction coefficient on polished steel | 0.36 | ||
Dry steel wear value | 0.13 | μm/km |
Thermal | Valore | Unità | Tipo di prova |
Melting point | 220 | °C | DIN EN ISO 3146 |
Thermal conductivity | 0.23 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.7 | J/(g*K) | |
Linear thermal expansion coefficient | 7 – 8 | 10–5*K–1 | |
Range of long-term use temperatures | -40+105 | °C | |
Range of operating temperatures for short periods | 180 | °C | |
Fire behavior | HB | UL 94 |
Electrical | Value | Unit | Test Type |
Dielectric constant | 3.7 | IEC 250 | |
Dielectric loss factor | 0.03 | IEC 250 | |
Volume resistance | 1015/1012 | Ω | IEC 93 |
Surface resistance | 1013/1012 | Ω*cm | IEC 93 |
Dielectric strength | 50 / 20 | kV/mm | IEC 243 |
Various | Value | Unit | Test Type |
Humidity absorption in saturated air | 2.2 | % | DIN 53715 |
Absorption of saturated water | 7 | % | DIN EN ISO 62 |
PA 6
PA 6
Material type: extruded thermoplastic polyamide
Features: good mechanical values, discrete impact and wear resistance, high humidity absorption, reduced dimensional stability compared to cast polyamide
Use: skids, guides, profiles, pulleys, pulleys, wheels, rollers
Assortment: round, tubes, plates, and drawing details.
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 1.14 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 70/45 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 50/180 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 2700/1800 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 2500/1400 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 130/40 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | >3/o.B. | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 160/70 | MPa | ISO 2039-1 |
Creep test di trazione 1% allungamento | >8 | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.38/0.42 | ||
Valore di usura a secco su acciaio | 0.23 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 218 | °C | ISO 3146 |
Conducibilità termica | 0.23 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.7 | J/(g*K) | |
Coefficiente di espansione termica lineare | 8-9 | 10-5 * K-1 | |
Gamma delle temperature di utilizzo per lungo periodo | -30 +100 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 140 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3.7 | IEC 250 | |
Fattore di perdita dielettrica | 0.031 | IEC 250 | |
Resistività di volume | 1015/1012 | Ω | IEC 93 |
Resistività di superficie | 1013/1012 | Ω*cm | IEC 93 |
Rigidità dielettrica | 50 / 20 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | 3 | % | DIN 53715 |
Assorbimento acqua a saturazione | 10 | % | ISO 62 |
PA 6/12
PA 6/12
Material type: polyamide 6/12, caprolactam mixture and lauryllactam
Characteristics: cast directly into the mould, compared to Pa6 G shows better shock resistance and reduced moisture absorption.
Use: gears, wheels in general, subject to high mechanical stress even in wet conditions
Assortment: round, plates, casting products and drawing details.
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 1.12 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 70/55 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 55/140 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 2500 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 2800 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 135 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | >12 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 140 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | >15 | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.36 | ||
Valore di usura a secco su acciaio | 0.12 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 220 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.23 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.7 | J/(g*K) | |
Coefficiente di espansione termica lineare | 7-8 | 10–5*K–1 | |
Gamma delle temperature di utilizzo per lungo periodo | -40+105 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 160 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3.7 | IEC 250 | |
Fattore di perdita dielettrica | 0.03 | IEC 250 | |
Resistività di volume | 1015 | Ω | IEC 93 |
Resistività di superficie | 1013 | Ω*cm | IEC 93 |
Rigidità dielettrica | 50 / 20 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | 1.9 | % | DIN 53715 |
Assorbimento acqua a saturazione | 5.8 | % | DIN EN ISO 62 |
PA 6G
PA 6G
Material type: cast thermoplastic polyamide
Characteristics: product by directly form polymerization, has a partially crystalline structure.
High crystallinity gives excellent mechanical properties such as good abrasion resistance, high wear resistance and good hardness and stiffness.
Use: skids, guides, profiles, pulleys, wheels, rollers, large size and volume parts
Assortment: rounds, tubes, plates, casting products and drawing parts
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 1.15 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 80/55 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 40/100 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 3100/1800 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 3400/2100 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 140/60 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | >4/>15 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 160/125 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | >7 | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.36/0.42 | ||
Valore di usura a secco su acciaio | 0.15 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 220 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.23 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.7 | J/(g*K) | |
Coefficiente di espansione termica lineare | 7-8 | 10-5*K-1 | |
Gamma delle temperature di utilizzo per lungo periodo | -40+105 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 170 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3.7 | IEC 250 | |
Fattore di perdita dielettrica | 0.03 | IEC 250 | |
Resistività di volume | 1015/1012 | Ω*cm | IEC 93 |
Resistività di superficie | 1013/1012 | Ω | IEC 93 |
Rigidità dielettrica | 50 / 20 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | 2.2 | % | DIN 53715 |
Assorbimento acqua a saturazione | 6.5 | % | DIN EN ISO 62 |
PA 6 G+Oil
PA 6 G+Oil
Material type: cast thermoplastic polyamide
Characteristics: when added with oil, it maintains the basic characteristics and properties, evident improvements in the sliding and abrasion resistance values.
Also approved for food use.
Use: large crowns, gears, various supports
Assortment: round, tubes, plates, casting products and drawing details.
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 1.14 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 75/60 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 50/120 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 2500 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 2800 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 135 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Res. all’urto con intaglio | >5 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 140 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | >7 | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.18 | ||
Valore di usura a secco su acciaio | 0.05 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 220 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.23 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.7 | J/(g*K) | |
Coefficiente di espansione lineare | 7-8 | 10–5*K–1 | |
Gamma delle temperature di utilizzo per lungo periodo | -40+105 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 160 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3.7 | IEC 250 | |
Fattore di perdita dielettrica | 0.03 | IEC 250 | |
Resistività di volume | 1015/1012 | Ω | IEC 93 |
Resistività di superficie | 1013/1012 | Ω*cm | IEC 93 |
Rigidità dielettrica | 50 / 20 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | 1.8 | % | DIN 53715 |
Assorbimento acqua a saturazione | 5.5 | % | DIN EN ISO 62 |
PE-HMW
PE-HMW
Type of material: partially crystalline thermoplastic with high molecular weight
Characteristics: good toughness and high resistance to chemical aggression. Highlights good smoothness, good load-bearing strength and low wear resistance due to creep resistance
Use: skids, chopping boards, logs, protections
Assortment: slabs and details to design.
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 0.95 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 28 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 300 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 850 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 850 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 40 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | 50 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 45 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | 3 | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.29 | ||
Valore di usura a secco su acciaio | 1.0 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 133 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.38 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.88 | J/(g*K) | |
Coefficiente di espansione lineare | 18 | 10–5*K–1 | |
Gamma delle temperature di utilizzo per lungo periodo | -100+50 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 80 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 2.9 | IEC 250 | |
Fattore di perdita dielettrica | 0.0002 | IEC 250 | |
Resistività di volume | > 1016 | Ω | IEC 93 |
Resistività di superficie | 1014 | Ω*cm | IEC 93 |
Rigidità dielettrica | 44 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | < 0.01 | % | DIN 53715 |
Assorbimento acqua a saturazione | < 0.01 | % | DIN EN ISO 62 |
PEEK
PEEK
Material type: extruded thermoplastic polyetheretherketone resin
Features: with excellent resistance to heat, wear, and radiation.
Good chemical resistance and hydrolysis (does not undergo substantial changes due to prolonged exposure to pressurized water at 250 ° C)
Employment: aeronautics, nuclear, oil industry. Medical equipment.
Assortment: rounds, tubes, plates and parts to design.
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 1.32 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 95 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 45 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 3600 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 4100 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 160 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | 7 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 230 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | – | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.34 | ||
Valore di usura a secco su acciaio | – | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 340 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.25 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.06 | J/(g*K) | |
Coefficiente di espansione lineare | 4-5 | 10-5*K-1 | |
Gamma delle temperature di utilizzo per lungo periodo | -40+250 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 310 | °C | |
Comportamento al fuoco | V-0 | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3.2 | IEC 250 | |
Fattore di perdita dielettrica | 0.0002 | IEC 250 | |
Resistività di volume | 1016 | Ω | IEC 93 |
Resistività di superficie | 1016 | Ω*cm | IEC 93 |
Rigidità dielettrica | 24 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | 0.2 | % | DIN 53715 |
Assorbimento acqua a saturazione | 0.45 | % | DIN EN ISO 62 |
PET GL
PET GL
Material type: partially crystalline thermoplastic polyester
Characteristics: adictivated with lubricants dispersed in the mass with important values of load resistance and very high self-lubricating characteristics, keeping wear resistance unchanged with respect to PET.
Use: plain bearings, bushings, cams, skids where high dimensional accuracy and high working loads are required.
Assortment: rounds, tubes, plates, and parts to design.
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 1.43 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 75 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 5 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 2200 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | – | MPa | DIN EN ISO 178 |
Resistenza a flessione | – | MPa | DIN EN ISO 178 |
Resistenza all’urto | 30 | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | 2 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | – | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | – | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.2 | ||
Valore di usura a secco su acciaio | 0.1 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 255 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.23 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | – | J/(g*K) | |
Coefficiente di espansione termica lineare | 7-8 | 10–5*K–1 | |
Gamma delle temperature di utilizzo per lungo periodo | -20+110 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 160 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3.6 | IEC 250 | |
Fattore di perdita dielettrica | 0,008 | IEC 250 | |
Resistività di volume | 1016 | Ω | IEC 93 |
Resistività di superficie | 1014 | Ω*cm | IEC 93 |
Rigidità dielettrica | – | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | 0.2 | % | DIN 53715 |
Assorbimento acqua a saturazione | 0.4 | % | DIN EN ISO 62 |
PP-H
PP-H
Type of material: crystalline thermoplastic polypropylene
Characteristics: very high level of resistance to chemical aggression even at temperatures up to 80°, can be used in conjunction with foodstuff, shows good rigidity hardness resistance, and one of the lowest specific gravity of plastic materials, excellent weldability.
Use: valves, flanges, fittings, pump parts, components used in the chemical industry
Assortment: round sheets and welded wire pipes
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 0,91 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 32 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 70 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 1400 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 1400 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 45 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | 7 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 70 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | 4 | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.35 | ||
Valore di usura a secco su acciaio | 11.00 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 162 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.22 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.7 | J/(g*K) | |
Coefficiente di espansione lineare | 16 | 10–5*K–1 | |
Gamma delle temperature di utilizzo per lungo periodo | 0+80 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 100 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 2.25 | IEC 250 | |
Fattore di perdita dielettrica | 0.00033 | IEC 250 | |
Resistività di volume | > 1016 | Ω | IEC 93 |
Resistività di superficie | 1014 | Ω*cm | IEC 93 |
Rigidità dielettrica | 52 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | < 0.01 | % | DIN 53715 |
Assorbimento acqua a saturazione | < 0.01 | % | DIN EN ISO 62 |
PA 6G+Solid lubricant
PA 6G+Solid lubricant
Type of material: melted thermoplastic polyamide
Characteristics: with addition of additives including lubricants and other noble fillers that optimize the value of the coefficient of friction and PV, always maintaining high wear resistance.
Use: bushings, pads, skids, rings, spacers, various parts where high wear resistance and low lubrication is required.
Use: bushings, pads, skids, rings, spacers, various parts where high wear resistance and low lubrication is required.
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 1.14 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 80/60 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 40/100 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 3100/1800 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 3300/2000 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 110/60 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | >4/>15 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 160/125 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | >7 | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.15/0.23 | ||
Valore di usura a secco su acciaio 3) | 0.08 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 220 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.23 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.7 | J/(g*K) | |
Coefficiente di espansione termica lineare | 7-8 | 10–5*K–1 | |
Gamma delle temperature di utilizzo per lungo periodo | -40+105 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 160 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3.7 | IEC 250 | |
Fattore di perdita dielettrica | 0.03 | IEC 250 | |
Resistività di volume | 1015/1012 | Ω | IEC 93 |
Resistività di superficie | 1013/1012 | Ω*cm | IEC 93 |
Rigidità dielettrica | 50 / 20 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | 2.2 | % | DIN 53715 |
Assorbimento acqua a saturazione | 6.5 | % | DIN EN ISO 62 |
PA 12G
PA 12G
Type of material: polyamide 12
Characteristics: cast directly in a vacuum mould, has good mechanical resistance, high impact resistance and remarkable chemical aggression resistance, high dimensional stability and reduced moisture absorption.
Use: bushings, wheels in general, particulars subject to high working loads in a particularly humid and / or combined medium medium temperature range
Assortment: rounds, slabs, casting products and customised parts.
Mechanics | Value | Unit | Test Type |
Density | 1.03 | g/cm3 | DIN EN ISO 1183 |
Yield load | 66 | MPa | DIN EN ISO 527 |
Elongation at break | 56 | % | DIN EN ISO 527 |
Traction elastic modulus | 2200 | MPa | DIN EN ISO 527 |
Flexible elastic modulus | 2400 | MPa | DIN EN ISO 178 |
Flexural resistance | 90 | MPa | DIN EN ISO 178 |
Bending resistance | N.R. | kJ/m2 | DIN EN ISO 179 |
Slotted impact resistance | >15 | kJ/m2 | DIN EN ISO 179 |
Hardness with penetration of the H358 / 30 ball | 100 | MPa | ISO 2039-1 |
Creep traction test: 1% elongation | >11 | MPa | DIN 53 444 |
Dynamic dry friction coefficient on polished steel | 0.4 | ||
Dry steel wear value 3) | – | μm/km |
Thermal | Valore | Unità | Tipo di prova |
Melting point | 190 | °C | DIN EN ISO 3146 |
Thermal conductivity | 0.23 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.7 | J/(g*K) | |
Linear thermal expansion coefficient | 10-11 | 10–5*K–1 | |
Range of long-term use temperatures | -60+110 | °C | |
Range of operating temperatures for short periods | 150 | °C | |
Fire behavior | HB | UL 94 |
Electrical | Value | Unit | Test type |
Dielectric constant | 3.7 | IEC 250 | |
Dielectric loss factor | 0.031 | IEC 250 | |
Volume resistance | 1015 | Ω | IEC 93 |
Surface resistance | 1013 | Ω*cm | IEC 93 |
Dielectric strength | 50 / 20 | kV/mm | IEC 243 |
Various | Value | Unit | Test type |
Humidity absorption in saturated air | 0.9 | % | DIN 53715 |
Absorption of saturated water | 1.4 | % | DIN EN ISO 62 |
PA 6.6
PA 6.6
Type of material: extruded thermoplastic polyamide
Characteristics: similar to Pa6E, with greater dimensional stability, stiffness, hardness and elastic modulus. Excellent sliding properties, electrical insulation and wear resistance. Poor impact resistance
Use: gears, bushings, rollers, saw-motor rollers, wheels, cams, washers, rings, valve seats, worm gears, spacers
Assortment: rounds, tubes, plates, and parts to design.
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 1.15 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 85/65 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 30/150 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 3200/1600 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 2900/1200 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 135/60 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Res. all’urto con intaglio | >3/>15 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 150/100 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | >8 | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.38/0.42 | ||
Valore di usura a secco su acciaio | 0,1 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 265 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.23 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.7 | J/(g*K) | |
Coefficiente di espansione termica lineare | 9-10 | 10–5*K–1 | |
Gamma delle temperature di utilizzo per lungo periodo | -30 +100 |
°C | |
Gamma delle temperature di utilizzo per breve periodo | 150 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3,2 | IEC 250 | |
Fattore di perdita dielettrica | 0,25 | IEC 250 | |
Resistività di volume | 1015/1012 | Ω | IEC 93 |
Resistività di superficie | 1012/1010 | Ω*cm | IEC 93 |
Rigidità dielettrica | 50 / 20 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | 2,5 | % | DIN 53715 |
Assorbimento acqua a saturazione | 9,00 | % | DIN EN ISO 62 |
PA 66 GF 30
PA 66 GF 30
Type of material: polyamide 6.6 extruded
Characteristics: added glass fibre that enhances the mechanical resistance characteristics in general and slightly increases the operating temperature, reducing moisture absorption in general
Use: parts requiring good dimensional stability and wear resistance
Assortment: rounds, slabs, and details to design.
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 1.35 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 160 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 5 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 11000 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | – | MPa | DIN EN ISO 178 |
Resistenza a flessione | – | MPa | DIN EN ISO 178 |
Resistenza all’urto | 30 | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | 2 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | – | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | – | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.02 | ||
Valore di usura a secco su acciaio | 0.01 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 255 | °C | DIN EN ISO 3146 |
Conducibilità termica | 00.23 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | – | J/(g*K) | |
Coefficiente di espansione lineare | 10-5*K-1 | ||
Gamma delle temperature di utilizzo per lungo periodo | -20+110 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 160 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3.06 | IEC 250 | |
Fattore di perdita dielettrica | 8 | IEC 250 | |
Resistività di volume | 1016 | Ω | IEC 93 |
Resistività di superficie | 1014 | Ω*cm | IEC 93 |
Rigidità dielettrica | – | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | 0.02 | % | DIN 53715 |
Assorbimento acqua a saturazione | 0.04 | % | DIN EN ISO 62 |
PA 6G+MOS2
PA 6G+MOS2
Type of material: melted thermoplastic polyamide
Characteristics: the properties of this material are substantially comparable to those of PA6G; thanks to the addition of molybdenum disulphide, abrasion/wear resistance and dynamic creep values are improved, without losing to the peculiar characteristics of cast polyamide.
Use: gears, bushings, pulleys, rollers, wheels, large wear parts, shoes, cams
Assortment: rounds, tubes, plates, casting products and customised parts.
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 1.15 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 85/60 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 40 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 3200/1850 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 3500/2200 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 145/70 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | >5/>15 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 170/130 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | >7 | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.32/0.37 | ||
Valore di usura a secco su acciaio | 0.15 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 220 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.23 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.7 | J/(g*K) | |
Coefficiente di espansione lineare | 7-8 | 10-5*K-1 | |
Gamma delle temperature di utilizzo per lungo periodo | -40+105 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 170 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3.7 | IEC 250 | |
Fattore di perdita dielettrica | 0.03 | IEC 250 | |
Resistività di volume | 1015/1012 | Ω | IEC 93 |
Resistività di superficie | 1013/1012 | Ω*cm | IEC 93 |
Rigidità dielettrica | 50 / 20 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | 2.2 | % | DIN 53715 |
Assorbimento acqua a saturazione | 6.5 | % | DIN EN ISO 62 |
PE-HD
PE-HD
Type of material: partially crystalline thermoplastic
Characteristics: good resistance to chemical aggression. Low load resistance, attractive sliding properties, low wear resistance due to creep, excellent weldability
Use: chopping boards, logs, protections, tanks, crates
Assortment: special round drawing slabs
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 0.95 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 22 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 300 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 800 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 800 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 32 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | 12 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 40 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | 3 | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.29 | ||
Valore di usura a secco su acciaio | 7.4 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 128 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.38 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.86 | J/(g*K) | |
Coefficiente di espansione lineare | 18 | 10-5 * K-1 | |
Gamma delle temperature di utilizzo per lungo periodo | -50+50 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 80 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 2.4 | IEC 250 | |
Fattore di perdita dielettrica | 0.004 | IEC 250 | |
Resistività di volume | > 1016 | Ω | IEC 93 |
Resistività di superficie | 1014 | Ω*cm | IEC 93 |
Rigidità dielettrica | 47 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | < 0.01 | % | DIN 53715 |
Assorbimento acqua a saturazione | < 0.01 | % | DIN EN ISO 62 |
PE-UHMW
PE-UHMW
Type of material: Partially crystalline thermoplastic with very high molecular weight
Features: Due to the high molecular weight it is superior to PEHD and PEHMW for flexural wear resistance values without any reduction in sliding values. Excellent kernel shock resistance values even at very low temperatures
Use: skids, gears, scrapers, spacers, ploughs, wheels
Assortment: round tubing slabs and drawing parts
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 0.94 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 22 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 350 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 800 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 800 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 27 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | o.B. | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 40 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | – | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.29 | ||
Valore di usura a secco su acciaio | 0.45 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 133 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.38 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.84 | J/(g*K) | |
Coefficiente di espansione lineare | 18 | 10–5*K–1 | |
Gamma delle temperature di utilizzo per lungo periodo | -260+50 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 80 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3.0 | IEC 250 | |
Fattore di perdita dielettrica | 0.0004 | IEC 250 | |
Resistività di volume | > 1016 | Ω | IEC 93 |
Resistività di superficie | 1014 | Ω*cm | IEC 93 |
Rigidità dielettrica | 44 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | < 0.01 | % | DIN 53715 |
Assorbimento acqua a saturazione | < 0.01 | % | DIN EN ISO 62 |
PET
PET
Type of material: extruded crystalline thermoplastic polyester
Features: matt natural colour with excellent dimensional stability, very low moisture absorption, outstanding dielectric properties.
High hardness and high wear and compression resistance
Use: particularly stressed bushings and roller bearings, gears, workpieces with tight tolerances can be manufactured.
Assortment: rounds, tubes, plates and parts to design.
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 1.38 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 80 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 20 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 3200 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 2600 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 125 | MPa | DIN EN ISO 178 |
Resistenza all’urto | 80 | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | >4 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 140 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | 13 | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.25 | ||
Valore di usura a secco su acciaio | 0.35 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 255 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.24 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.1 | J/(g*K) | |
Coefficiente di espansione termica lineare | 7-8 | 10–5*K–1 | |
Gamma delle temperature di utilizzo per lungo periodo | -20+100 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 160 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3.6 | IEC 250 | |
Fattore di perdita dielettrica | 0.008 | IEC 250 | |
Resistività di volume | 1016 | Ω | IEC 93 |
Resistività di superficie | 1014 | Ω*cm | IEC 93 |
Rigidità dielettrica | 40 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | 0.25 | % | DIN 53715 |
Assorbimento acqua a saturazione | 0.5 | % | DIN EN ISO 62 |
POM C
POM C
Type of material: extruded polyoxyMethylene thermoplastic
Features: High level of stability and stiffness and good sliding properties and wear resistance, low moisture absorption, good dimensional stability, fatigue resistance, excellent machinability to the machine tool.
Use: bushings, gears, nozzles, pusher valve housings, rollers also operating in wet environments
Assortment: rounds, tubes, plates and parts to design
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 1.41 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 65 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 40 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 3000 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 2900 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 115 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | >10 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 150 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | 13 | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.32 | ||
Valore di usura a secco su acciaio | 8.9 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 168 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.31 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1.45 | J/(g*K) | |
Coefficiente di espansione termica lineare | 9-10 | 10–5*K–1 | |
Gamma delle temperature di utilizzo per lungo periodo | -30+100 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 140 | °C | |
Comportamento al fuoco | HB | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3.9 | IEC 250 | |
Fattore di perdita dielettrica | 0.003 | IEC 250 | |
Resistività di volume | 1015 | Ω | IEC 93 |
Resistività di superficie | 1013 | Ω*cm | IEC 93 |
Rigidità dielettrica | 40 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | 0.2 | % | DIN 53715 |
Assorbimento acqua a saturazione | 0.8 | % | DIN EN ISO 62 |
PTFE
PTFE
Type of material: extruded polytetrafluoroethylene thermoplastic
Features: known for its strong resistance to chemical aggression and very high temperatures, but also for its reduced mechanical characteristics, reduced compressive and wear resistance and low dimensional stability, it shows a higher specific weight compared to other plastics.
Use: seals, sealing rings, heat protectors, skids, scrapers, used also at high temperature
Assortment: round tubes, sleeves and plates and drawing details
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 2.18 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 10 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 380 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 750 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | 540 | MPa | DIN EN ISO 178 |
Resistenza a flessione | 6 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | 16 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 30 | MPa | ISO 2039-1 |
Creep test di trazione: 1% allungamento | 1.5 | MPa | DIN 53 444 |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.08 | ||
Valore di usura a secco su acciaio | 21.00 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | 327 | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.23 | W/(K*m) | DIN 52 612 |
Specific thermal capacity | 1 | J/(g*K) | |
Coefficiente di espansione lineare | 18-20 | 10–5*K–1 | |
Gamma delle temperature di utilizzo per lungo periodo | -200+260 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 280 | °C | |
Comportamento al fuoco | V-0 | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 2.1 | IEC 250 | |
Fattore di perdita dielettrica | 0.0005 | IEC 250 | |
Resistività di volume | 1018 | Ω | IEC 93 |
Resistività di superficie IEC 93 | 1017 | Ω*cm | IEC 93 |
Rigidità dielettrica | 40 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | < 0.01 | % | DIN 53715 |
Assorbimento acqua a saturazione | < 0.01 | % | DIN EN ISO 62 |
PVC-U
PVC-U
Type of material: PVC-U VINILE CLORATE RIGID “PVC-U”.
Features: rigid PVC has high chemical stability and excellent fire resistance (it is self-extinguishing). Rigid PVC has an amorphous structure, high solidity and a high modulus of elasticity. It has excellent electrical characteristics, especially in the low voltage and frequency range.
Used with temperatures between – 10°c and + 60°c. Rigid PVC is stable at temperatures of up to 60°c at most diluted or concentrated acids. It is a good electrical insulator and absorbs little water; it can also be welded and bonded.
Use: rings, spacers, supports, supports, wheels, insulators, heels, heels, thicknesses, spacers.
Assortment: round tubes, sheet sleeves and drawing details
Meccaniche | Valore | Unità | Tipo di prova |
Densità | 1,42 | g/cm3 | DIN EN ISO 1183 |
Carico di snervamento | 58 | MPa | DIN EN ISO 527 |
Allungamento a rottura | 15 | % | DIN EN ISO 527 |
Modulo elastico a trazione | 3000 | MPa | DIN EN ISO 527 |
Modulo elastico a flessione | – | MPa | DIN EN ISO 178 |
Resistenza a flessione | 82 | MPa | DIN EN ISO 178 |
Resistenza all’urto | N.R. | kJ/m2 | DIN EN ISO 179 |
Resistenza all’urto con intaglio | 4 | kJ/m2 | DIN EN ISO 179 |
Durezza con penetrazione della sfera H358/30 | 130 | MPa | |
Creep test di trazione: 1% allungamento | – | MPa | DIN 53 444 2) |
Coefficiente di attrito dinamico a secco su acciaio lucido | 0.6 | ||
Valore di usura a secco su acciaio | 56.0 | μm/km |
Termiche | Valore | Unità | Tipo di prova |
Temperatura di fusione | – | °C | DIN EN ISO 3146 |
Conducibilità termica | 0.156 | 10–5*K–1 | DIN 52 612 |
Specific thermal capacity | 1.05 | J/(g*K) | |
Coefficiente di espansione lineare | 8 | 10-5 * K-1 | |
Gamma delle temperature di utilizzo per lungo periodo | -10+60 | °C | |
Gamma delle temperature di utilizzo per breve periodo | 70 | °C | |
Comportamento al fuoco | V-0 | UL 94 |
Elettriche | Valore | Unità | Tipo di prova |
Costante dielettrica | 3.3 | IEC 250 | |
Fattore di perdita dielettrica | 0.025 | IEC 250 | |
Resistività di volume | 1016 | Ω | IEC 93 |
Resistività di superficie | 1016 | Ω*cm | IEC 93 |
Rigidità dielettrica | 39 | kV/mm | IEC 243 |
Varie | Valore | Unità | Tipo di prova |
Assorbimento umidità in aria a saturazione | <0.01 | % | DIN 53715 |
Assorbimento acqua a saturazione | <0.01 | % | DIN EN ISO 62 |
** The titles and data provided in the tables are for information only and do not imply any liability on the part of UFG srl.